Method for Siliconizing Carbon-Containing Materials

ABSTRACT

A method for treating workpieces that consist of porous carbon material with liquid silicon with the formation of silicon carbide, comprising the steps: Preheating porous carbon workpieces under inert gas to the selected operating temperature T B 1, feeding liquid silicon to the porous carbon workpieces at an operating pressure p B 2 and an operating temperature T B 2, and impregnating the porous carbon workpieces with liquid silicon, reaction of the liquid silicon in the workpiece at a temperature T B 3 with the formation of silicon carbide that consists of carbon and silicon, gassing the workpiece with inert gas and cooling from the operating temperature T B 3 to the conditioning temperature T k , cooling the workpieces to room temperature, the temperature T B 3 being greater than or equal to the temperature T B 2, and the workpiece in step d of the method no longer being in contact with liquid silicon outside of the workpiece.

This invention relates to a method for siliconizing carbon-containing materials and a device that is adapted for this purpose.

A method for siliconizing carbon materials was described by a working group of DLR (Deutsche Forschungsanstalt für Luft- und Raumfahrt e.V. [German Research Institute for Air and Space Travel e.V.]), Stuttgart, Institut für Bauweisen- und Konstruktionsforschung [Institute for Construction and Design Research], in the VDI [Association of German Engineers] Materials Conference in Duisburg on Mar. 9-10, 1994. Carbon materials, reinforced with fibers that consist of carbon, were infiltrated therein with melted silicon in a so-called “liquid siliconization method.” By heat treatment, the elementary silicon reacts with the carbon to form silicon carbide. Structural components and in particular friction elements for brake and clutch systems in automobiles can be produced from such materials.

Similar methods are described in, for example, EP 0 956 276, with the carbon work pieces that are to be siliconized and suitably bonded powdery silicon being heated together; the melted silicon penetrates the carbon workpieces and reacts at least partially with the carbon to form silicon carbide.

All known methods are, however, batch methods; in the past, only batch-type conversion of carbon materials into materials with a silicon carbide-containing matrix was possible. In this case, the furnaces in which the silicon is melted and in which the reaction of liquid silicon with carbon to form silicon carbide is performed must first be charged, heated up under inert gas atmosphere and optionally evacuated, cooled after the reaction to form silicon carbide at the necessary holding time, and unloaded. Such a method requires long heating and cooling times and is inefficient in terms of energy use.

The object is therefore to indicate a method with which a treatment, to be operated semi-continuously, of workpieces that optionally consist of fibers, preferably of carbon, reinforced porous carbon with liquid silicon with at least partial conversion to silicon carbide, is possible.

The object is achieved by a method that comprises the following steps:

a Preheating porous carbon workpieces under inert gas to the selected operating temperature T_(B)1,

c Feeding liquid silicon to the porous carbon workpieces at an operating pressure p_(B)2 and an operating temperature T_(B)2, and impregnating the porous carbon workpieces with liquid silicon,

d Reaction of the liquid silicon in the workpiece at a temperature T_(B)3 with the formation of silicon carbide that consists of carbon and silicon,

e Gassing the workpiece with inert gas and cooling from the operating temperature T_(B)3 to the conditioning temperature T_(k)

f Cooling the workpieces to room temperature,

the temperature T_(B)3 being greater than or equal to the temperature T_(B)2, and the workpiece in step d of the method no longer being in contact with liquid silicon outside of the workpiece.

In a preferred way, an additional step

b Reduction of the pressure to the operating pressure p_(B)1 can be inserted between steps a and c, whereby the reduction of the pressure can be carried out before or after the heating or during the heating, but always after the step of rinsing with inert gas.

Another subject of this invention is an adapted device for implementing the method, consisting of at least four chambers O1 to O4, which are connected to one another by locks, whereby each of the chambers, independently of its neighbors, can be heated, cooled, evacuated and filled or rinsed with suitable gases. In this context, each of the chambers O₁ is provided with at least one transporting or conveying device, with whose assistance the workpieces are transported from the previous chamber O_(i=1) into the chamber O_(i) and from the chamber O_(i) into the subsequent chamber O_(i+1), in the configuration with 4 chambers, for example, O_(i=0) being the inlet and O_(i=5) being the outlet from the configuration consisting of four chambers. In the case of four chambers, the index i can assume the values 1, 2, 3 and 4. The inlet (first lock) and the outlet (last lock) are referred to here as O0 and O5 for simplification.

Spatial separation of the individual steps of the method and clocklike semi-continuous conveying, of the workpieces in chambers that are separated from one another and from the environment by locks make it possible to allow the operating conditions (temperature, pressure) in the individual chambers to be as constant as possible; this results in uniform operating conditions, reduction of the energy demand, and greater flexibility in production. Conveying or transporting of the workpieces can be carried out by means and methods that are known in the art, for example by sliding or conveying by means of a slide, by transport on rollers, by means of one or more lifting bars, or on a plain coil chain. In this case, materials are used for the transport means that withstand the selected temperatures and the media that are used, for example selected from graphite and other carbon materials that can be reinforced with fibers, e.g., made of carbon, and also materials that consist of boron nitride or refractory materials that are coated with boron nitride.

In this context, steps a and b as well as steps d and e can be performed in each case in a common chamber, while at least one separate chamber is otherwise provided for each of the steps of the method.

The heating in the chambers is carried out with known heating devices, in particular infrared radiators, inductive heaters, microwave heaters and heating by heated gas (inert gas). Cooling is carried out by a cooled flow of gas flowing through the chamber in question, at higher temperatures, inert gases such as nitrogen and argon being preferred, while at temperatures of no more than 300° C., air can also be used.

By preference an induction heater in the chamber O1 is used, since this type of heater can very quickly introduce large amounts of energy into the workpiece.

The device will be explained using the drawings.

FIG. 1 shows a diagrammatic section through a configuration with four chambers; to improve the clarity, the feed and exhaust cycles are not indicated for the gases that are used,

FIG. 2 a shows a cutaway of the second chamber O2 according to FIG. 1, with the detailed representation of the positioning of the workpiece 95 on (two shown) preferably porous wicks 26, which guide the liquid silicon to the workpiece 95,

FIG. 2 b shows a cutaway of the chamber O2 according to FIG. 2 a, with the detailed representation of an alternative embodiment, the workpiece itself having a molded-on fitting 201, and

FIG. 2 c shows an enlarged section through a workpiece with a molded-on fitting 201.

According to the invention, the procedure is preferably carried out in a device, shown in FIG. 1, that consists of four chambers, so that the workpieces are inserted in succession into the first chamber O1 by the lock 10 from outside, here represented as the next to be inserted and referred to as 91, 92 and 93. After closing the lock 10. the chamber O1 is flushed according to step a of the method with a wave of inert gas, preferably with nitrogen or argon, and after the displacement of the air by means of optionally several sequences of inert gas flushing and evacuation, the workpiece 94 that is already located in the chamber is preferably heated by an induction heater 11 from room temperature to the operating temperature T_(B)1, which can be from 1300° C. to 1800° C., preferably 1350° C. to 1750° C. In a preferred way, the operating pressure is reduced by 1 bar (outside pressure, 10⁵ Pa) to a value p_(B)1 of preferably no more than 100 mbar (100 hPa), especially preferably up to 50 hPa (50 mbar), and in particular no more than 20 mbar (20 hPa). This reduction of the pressure according to step b of the method can be carried out before heating, during heating or after heating.

At the latest before the lock 20 is opened, a negative pressure is produced in the chamber O1, as it also preferably constantly prevails in chamber O2, preferably below 10 hPa (10 mbar), in particular below 1 Pa (10⁻² mbar).

If this pressure is reached, the workpiece is transported by the lock 20 into the chamber O2, where it is now referred to as 95. After the lock 20 is closed, a new workpiece is inserted from outside by the lock 10 into the chamber O1 and heated as described above.

In the chamber O2, the workpiece 95 is taken up at an operating pressure p_(B)2 of no more than about 10⁻² mbar (1 Pa) and at an operating temperature T_(B)2 that can be adjusted via the heater 21 from 1450° C. to 1700° C. by a transport device, not shown, and placed on the supports (porous wicks) 26 that are mounted in the siliconizing device 27. In this siliconizing device 27, liquid silicon 25 that is located in a basin 22 according to step c of the method moves into the workpiece 95 that consists of carbon via the porous wicks 26, At the temperature prevailing in the chamber, of between 1450° C. and 1700° C., silicon penetrates into the pores of the workpiece 95 and reacts at least partially according to step d of the method with the carbon that is present in the workpiece to form silicon carbide. The workpiece is referred to as “siliconized workpiece” after this treatment.

In a preferred embodiment, the basin 22 is placed in the chamber O2 on one or more (two in number shown in the drawing of FIG. 2 a) pressure measuring cells 28; this makes it possible to determine the mass of the silicon taken up in the workpiece by weighing the basin before the attachment of the workpiece 95 and after the infiltration and the removal of the workpiece 95.

After the siliconization, the siliconized workpiece 95 is raised from the wicks and transported by the lock 30 into the chamber O3.

After each clock cycle (removal of a siliconized workpiece 95 from O2 and input of a freshly preheated workpiece from the chamber O1), the level of the liquid silicon in the basin 22 is made up again to the preset value; to this end, a reservoir 23 with liquid silicon, which is connected by a pipe 24 to the basin 22, is used.

In the chamber O3, optionally by further heating with the heater 31, the reaction is completed to the desired extent according to step d of the method in the siliconized workpiece, whereby the spatial separation of the chamber O2 produces the advantageous possibility of annealing the workpiece in the chamber O3 even at a temperature T_(B)3 above the temperature T_(B)2 without running the risk of silicon escaping from the basin 22 as in the selection of a higher temperature in the chamber O2 by the higher vapor pressure. It was noted namely in the tests upon which this invention was based that the silicon penetrates into the pores of the workpiece (now 96) has a considerably lower vapor pressure compared to the silicon in the bath 22 at the same temperature.

A preferred temperature range for such an after-reaction is that of 1500° C. to 2000° C., especially preferably 1600° C. to 1900° C. and in particular 1700° C. to 1800° C. The formation of the silicon carbide can proceed considerably faster, which results in a desirable shortening of the cycle times in the method according to the invention.

Heating in the chambers O2 and O3 is canned out preferably by a radiant heater, for example with graphite heating elements 21 and 31 that are brought to annealing by Joule heating.

As soon as the reaction to form silicon carbide is carried out to the desired extent, the workpiece is cooled in the chamber O3 by blowing in cold inert gas according to step e of the method, preferably to a conditioning temperature T_(K) in the range of 500° C. to 300° C. The operating pressure p_(B)3 in this case increases from initially (after-reaction) below 1 mbar (1 hPa) to normal pressure (10⁵ Pa=1 bar). Then, the workpiece 96 is brought through the lock 40 into the chamber O4 and further cooled to room temperature there in the position 97 according to step f of the method, first with inert gas, starting from temperatures of no more than 300° C., and also with air. The finished workpiece 98 can then be removed by the lock 50.

Of course, before the next workpiece 95 is conveyed into the chamber O3 for the after-reaction, this chamber O3 is again evacuated to the operating pressure p_(B)3.

In the method according to the invention, in an embodiment with four chambers, a dwell time of workpieces in the chambers O1 to O4 of three minutes up to twenty minutes in each case has proven advantageous.

The method according to the invention ensures that the workplaces 95 that are brought into the chamber O2 for siliconization are always brought to the operating temperature prevailing in O2 and that the operating pressure in O2 is always maintained. This uniformity of pressure and temperature in the siliconization step has proven essential for reaching a constant product quality. Another advantage is that the workpieces are not cooled in contact with the silicon bath, and this keeps pores that are formed during cooling by volume contraction of silicon from being filled by subsequently suctioned-off silicon.

If several steps of the method are performed in one of the chambers, for example in O3, the stage of the after-reaction, which optionally is carried out at an elevated temperature compared to O2, and then the cooling, it is further preferred to subdivide these chambers. In the case of O3, such a subdivision according to steps d and e of the method are provided, first to perform the after-reaction at the higher temperature and then to bring the workpiece in turn through a lock in an additional chamber configured between O3 and O4 for cooling. In this way, it is achieved that the chamber O3 can be operated at a constant temperature, and the chambers configured between O3 and O4 are used only for cooling.

It is also possible to configure two chambers behind one another with the same step of the method if the necessary dwell time for a step of the method deviates considerably from that for the other steps in the method, in this way achieving a uniform clock cycle for all chambers. The minimum number of chambers necessary for the method is four.

In another embodiment, the workpieces 9 have molded-on fittings 201 on a flat side, these fittings 201 having a tapering section on this flat side as is shown in FIG. 2 b and enlarged in FIG. 2 c, These fittings 201 dip into the liquid silicon 25 in the silicon bath 27 or are on the supports 29, After the finished workpieces are removed from the device, these fittings 201 can easily be broken off, since the extent of the tapering section is selected to make this possible.

It Is also possible, of course, to use alloys or liquid mixtures of silicon with one or more other elements for infiltration instead of pure silicon. In particular, additives of iron (in a percentage by mass of up to 6% in the mixture), refractory metals, such as chromium, molybdenum, tungsten, zirconium (in a percentage by mass of up to 3% in the mixture in each case) as well as manganese, aluminum, cobalt and nickel (in a percentage by mass of up to 3% in the mixture in each case) have proven their value.

LIST OF REFERENCE DESIGNATIONS

O1 Chamber 1

O2 Chamber 2

O3 Chamber 3

O4 Chamber 4

10 Lock

11 Induction Heater

20 Lock

21 Heater

22 Basin

23 Reservoir with Liquid Silicon

24 Pipe

25 Liquid Silicon

26 Wicks

27 Siliconizing Device

28 Pressure measuring ceil

29 Supports

30 Lock

31 Heater

40 Lock

50 Lock

91,92,93 Workpieces

94 Workpiece in Chamber O1

95 Siliconized Workpiece in Chamber O2

96 Siliconized Workpiece in Chamber O3

97 Siliconized Workpiece in Chamber O4

98 Finished Siliconized Workpiece 

1. (canceled)
 2. (canceled)
 3. (canceled)
 4. (canceled)
 5. (canceled)
 6. (canceled)
 7. (canceled)
 8. (canceled)
 9. A device for implementing a method for treating workpieces, the workpieces consisting of porous carbon material with liquid silicon with the formation of silicon carbide, the method comprising the steps: a) preheating porous carbon workpieces under inert gas to the selected operating, temperature T_(B)1, b) dropping the pressure to an operating pressure p_(B)1 of no more than 100 hPa. c) feeding liquid silicon to the porous carbon workpieces at an operating pressure p_(B)2 and an operating temperature T_(B)2, and impregnating the porous carbon workpieces with liquid silicon. d) reacting the liquid silicon in the workpiece at a temperature T_(B)3 with the formation of silicon carbide, e) gassing the workpiece with inert gas and cooling from the operating temperature T_(B)3 to the conditioning temperature T_(k), and f) cooling the workpieces to room temperature. wherein the temperature T_(B)3 is greater than or equal to the temperature T_(B)2, and the workpiece in the step c) is not in contact with liquid silicon outside of the workpiece, the device comprising at least four chambers, wherein each chamber is optionally heated, cooled, evacuated, and rinsed with gases separately from one another, wherein the chambers are connected to one another by locks. wherein, in an embodiment with four chambers, in each case one chamber being provided for steps c and f of the method and in each case one chamber being provided for steps a and b, as well as steps d and e of the method to be implemented in succession in each case; wherein, in an embodiment with five chambers, in each case separate chambers for steps a and b of the method or steps d and e of the method being provided; and wherein, in an embodiment with six chambers, in each case a separate chamber being provided for all steps a, b, c, d. e, and f in each case.
 10. The device according to claim 9, wherein in each case at least two chambers are provided for at least one of steps a to f.
 11. An apparatus comprising four chambers connected in series by a plurality of locks, wherein the second chamber comprises a siliconizing device having a basin and at least one wick disposed within the basin, and wherein the wick is positioned to contact both the workpiece and a liquid held within the basin.
 12. The apparatus of claim 11, wherein the first chamber comprises an inlet lock through which the workpiece can be inserted, and a first heater for heating the workpiece from room temperature to a temperature of from 1300 to 1800° C.
 13. The apparatus of claim 11, wherein the second chamber further comprises a second heater for heating the workpiece to a temperature of from 1450 to 1700° C., and wherein the second chamber is operated at a negative internal pressure.
 14. The apparatus of claim 11, wherein the third chamber comprises a third heater capable of maintaining the workpiece at a temperature of from 1500 to 2000° C., and a gas inlet for cooling the workpiece to a conditioning temperature in the range of from 300 to 500° C.
 15. The apparatus of claim 11, wherein the fourth chamber comprises a gas inlet for cooling the workpiece to room temperature, and an outlet lock through which the workpiece can be removed.
 16. The apparatus of claim 11, wherein the first heater is selected from the group consisting of an infrared radiator, an inductive heater, a microwave heater, and a supply of heated gas.
 17. The apparatus of claim 11, wherein the first heater is an induction heater.
 18. The apparatus of claim 11, wherein the second heater is a radiant heater.
 19. The apparatus of claim 11, wherein the third heater is a radiant heater.
 20. The apparatus of claim 11, further comprising a silicon reservoir connected by a pipe to the basin of the siliconinzing device.
 21. The apparatus of claim 11, further comprising a conveyor for transporting a workpiece between the chambers. 